This paper deals with the fatigue strength of S355NL steel, of a common use within the shipbuilding industry, under uniaxial constant and variable loading. Indeed, ship structures are subjected to variable loading due to various sea states, wind and waves. As a consequence, a better knowledge of fatigue behavior under real loading conditions is needed. This study aims at analyzing the influence of loading conditions (load ratio and variable amplitude loading) on the short crack behavior and last, with a proposed model to assess the fatigue crack life. The tools used to prepare inspections in critical areas only take into account the long crack behavior. The results from the proposed model were compared to the assessments these tools are providing with.
Short surface fatigue cracks growth under constant and variable amplitude loading
Oberflächen-Ermüdungskurzrisswachstum bei konstanter und Belastung mit variabler Amplitude
Engineering Fracture Mechanics ; 76 , 15 ; 2359-2370
2009
12 Seiten, 26 Quellen
Aufsatz (Zeitschrift)
Englisch
Low Cycle Fatigue of Spot Welds Under Constant and Variable Amplitude Loading
British Library Conference Proceedings | 2003
|Fatigue and Crack Growth in 7050-T7451 Aluminum Alloy Under Constant- and Variable-Amplitude Loading
Online Contents | 2013
|Low Cycle Fatigue of Spot Welds Under Constant and Variable Amplitude Loading
SAE Technical Papers | 2003
|