The design of pipelines to resist ductile fracture propagation has traditionally utilised semiempircal models based on Charpy V-notch impact energy. Recent full-scale fracture propagation tests have shown these methods to fall short in characterising the fracture behaviour of high strength steels such as Grade X100 and over. So, there is a general opinion that the Charpy-V fracture parameter exhibits some intrinsic limitations that preclude its use when high strength steels are considered. This paper focuses on the existing proposed methods to define the laboratory toughness of steels and on the limitations encountered when characterising the real ductile fracture propagation behaviour of high grade steel pipes.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Existing methods to evaluate fracture resistance of high grade steel pipelines


    Beteiligte:
    Demofonti, G. (Autor:in) / Mannucci, G. (Autor:in) / Roovers, P. (Autor:in)

    Erschienen in:

    Drei R International ; 48 , Special 1: Pipeline Technology ; 5-8


    Erscheinungsdatum :

    2009


    Format / Umfang :

    4 Seiten, 4 Bilder, 16 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Deutsch




    Effect of grade on ductile fracture arrest criteria for gas pipelines

    Wilkowski, G. / Rudland, D. / Xu, H. et al. | Tema Archiv | 2007


    Corrosion control methods that extend the life of existing pipelines

    Szeliga, M.J. / Simpson, D.M. | Tema Archiv | 1999


    Development of high toughness X70 grade clad steel pipe for natural gas transportation pipelines

    Kayano, Rinzo / Nitta, Yukio / Sato, Shinya et al. | Tema Archiv | 2007


    Fracture toughness of grade D ship steel

    Sumpter, J.D.G. / Kent, J.S. | Tema Archiv | 2006