To assess potential routes for the production of high-strength Al 5083, gas-atomized powder was cryogenically ball-milled, to obtain a nanocrystalline structure, then hot vacuum degassed and consolidated by two methods: (1) hot isostatic pressing (HIPping) and extrusion, and (2) two-step quasi-isostatic (QI) forging. The consolidated billet in both cases was hot-rolled to produce 19 mm plate. Despite grain growth and differences in the consolidation and deformation processing, a similar, ultra-fine grained microstructure was obtained in both plates, with elongated grains predominantly in the range 100-500 nm. The cryomilled plates had similar tensile strengths in the plane of the plate, which were up to 60% greater than conventionally processed and work-hardened Al 5083. However, the QI-forged plate had significantly higher fracture toughness than the HIP/extruded plate, which was brittle for crack surfaces in the plane of the plate. The disparity in toughness values was attributed to differences in the prior powder particle boundary structure.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Large UFG AI alloy plates from cryomilling


    Beteiligte:
    Newbery, A.P. (Autor:in) / Ahn, B. (Autor:in) / Topping, T.D. (Autor:in) / Pao, P.S. (Autor:in) / Nutt, S.R. (Autor:in) / Lavernia, E.J. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2008


    Format / Umfang :

    9 Seiten, 6 Bilder, 4 Tabellen, 15 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Effect of Cryomilling on Microstructure and Mechanical Properties of 7050 Aluminum Alloy

    ZHANG Haiping / WANG Xudong / LI Jiongli et al. | DOAJ | 2018

    Freier Zugriff

    Metastable Aluminum-Based Reactive Composite Materials Prepared by Cryomilling

    Zhang, S. / Schoenitz, M. / Dreizin, E. et al. | British Library Conference Proceedings | 2012


    Metastable Aluminum-Based Reactive Composite Materials Prepared by Cryomilling

    Zhang, Shasha / Schoenitz, Mirko / Dreizin, Edward | AIAA | 2012


    Large Deflection of curved plates

    Lew, H G / Fox, J A / Loo, T T | NTRS | 1956


    Large deflection of curved plates

    Lew, H. G. / Fox, J. A. / Loo, T. T. | TIBKAT | 1956