A new high Mn-Ni free (duplex stainless steel) DSS containing 18Cr-6Mn-1Mo-0.2N has been developed by examining the effects of manganese on the corrosion and mechanical properties of high Mn SSs containing 18Cr-4~11Mn-0~2Ni-0~1Mo-0.2N. The alloy with 45% ferrite is found to be an optimum alloy with much higher mechanical strength and similar corrosion resistance compared with those of standard SS304, at an economical cost. In addition, the alloy was free of precipitation of sigma phase and Cr-nitride when exposed to high temperatures due primarily to relatively low contents of Cr, N and Mo. With an increase in Mn content, the resistance to pitting and metastable pitting corrosion of high Mn DSS decreased since the number of (Mn, Cr) oxides, acting as preferential sites of pitting, increased with the Mn content.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Development of high Mn-N duplex stainless steel for automobile structural components


    Weitere Titelangaben:

    Entwicklung von nichtrostendem Duplexstahl mit hohem Mn-N-Anteil für tragende Automobilbauteile


    Beteiligte:

    Erschienen in:

    Corrosion Science ; 50 , 2 ; 404-410


    Erscheinungsdatum :

    2008


    Format / Umfang :

    7 Seiten, 8 Bilder, 1 Tabelle, 41 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Sustanaible duplex stainless steel bridges

    Baddoo, N.R. / Kosmac, A. | Tema Archiv | 2010


    Duplex stainless steel for pipeline applications

    Singh, A.K. / Bagdasarian, A.J. | Tema Archiv | 1987


    Underwater Welding of Duplex Stainless Steel

    Labanowski, Jerzy / Fydrych, Dariusz / Rogalski, Grzegorz et al. | Tema Archiv | 2011