Data for long-term marine immersion and half-tide corrosion loss and pitting of chromium-bearing and stainless steels is systematically re-examined and re-interpreted to show that it is consistent with the model previously proposed for mild and low-alloy steel corrosion. Early corrosion of chromium-bearing steels is well known to be influenced by bacterial activity in the biofilm adjacent to the metal surface. However, the effect appears short-lived and typically the corrosion rate declines, presumably due to the buildup of corrosion products, either on the surface or within pits. The data considered herein show that after some two to four years of exposure there is usually a considerable increase in the instantaneous corrosion rate both for weight loss and for pitting. This is interpreted in terms of the previously proposed model for the corrosion of steels as the result of bacterial activity but now located primarily within pits and crevices. This interpretation implies that the early and the later corrosion processes involve different mechanisms and that corrosion loss and pit depth data are not all from the same homogeneous population. As a result, the prediction of long-term corrosion from short-term laboratory or field observations is of doubtful validity. This has important implications for the prediction of the effective life of chromium bearing and stainless steels in infrastructure applications.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Modeling of long-term corrosion loss and pitting for chromium-bearing and stainless steels in seawater


    Weitere Titelangaben:

    Modellierung des Langzeit-Korrosionsverlustes und der Lochkorrosion von chromhaltigem Lagermetall und nichtrostenden Stählen in Meerwasser


    Beteiligte:
    Melchers, R.E. (Autor:in) / Jeffrey, R. (Autor:in)

    Erschienen in:

    Corrosion, Houston ; 64 , 2 ; 143-154


    Erscheinungsdatum :

    2008


    Format / Umfang :

    12 Seiten, 13 Bilder, 2 Tabellen, 35 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Investigation of pitting corrosion behaviour of welded duplex stainless steels

    Gobbon,M.E. / Univ.d.Bundeswehr Hamburg,DE | Kraftfahrwesen | 1994


    Pitting corrosion and crevice corrosion behaviors of high nitrogen austenitic stainless steels

    Li, H. b. / Jiang, Z. h. / Yang, Y. et al. | British Library Conference Proceedings | 2009



    Nitrogen-bearing stainless steels: cost-effective materials for seawater service

    Latha, G. / Rajendran, N. / Rajeswari, S. | Tema Archiv | 1998


    Corrosion behavior of some highly alloyed stainless steels in seawater

    Malik, A.U. / Siddiqi, N.A. / Andijani, I.N. | Tema Archiv | 1994