Crevice corrosion behavior of high nitrogen-bearing stainless steels with up to 1.1 mass% nitrogen were investigated in artificial seawater. Specimens were highly purified and contained ultra-high nitrogen of about 1 mass% obtained by using nitrogen gas pressurized electroslag remelting (P-ESR) system. 23%Cr-4%Ni-0 to 2%Mo-0.7 to 1.1 %N stainless steels were used as test specimens. Crevice corrosion resistant proper-ties of the stainless steels were evaluated by means of electrochemical corrosion test method using multi-ple crevice assemblies. Crevice corrosion was confirmed by visual observation to be generated after test and by in-situ current response under test. It was seen that there was a positive correlation between nitro-gen content and crevice corrosion potential. High nitrogen-bearing austenitic stainless steels produced by P-ESR had good crevice corrosion resistance. It was also found that ultra-high nitrogen stainless steels con-taining molybdenum had superior crevice corrosion resistance. Surface of high nitrogen stainless steel was analyzed using X-ray photoelectron spectroscopy (XPS). After polarization at the passive potential region (at + 300 mV vs. SCE), an alloying nitrogen or nitride peak of N1s spectra appeared at higher take-off angle measurement, indicating that nitrogen concentrated at the inner layer of the interface between passive film and bulk metal. Enriched nitrogen at the interface may be possible to improve crevice corrosion resistance.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Localized corrosion behavior of high nitrogen-bearing austenitic stainless steels in seawater environment


    Weitere Titelangaben:

    Örtliches Korrosionsverhalten von hochstickstoffhaltigen austenitischen nichtrostenden Stählen in Meerwasserumgebung


    Beteiligte:
    Sagara, M. (Autor:in) / Katada, Y. (Autor:in) / Kodama, T. (Autor:in)

    Erschienen in:

    ISIJ International ; 43 , 5 ; 714-719


    Erscheinungsdatum :

    2003


    Format / Umfang :

    6 Seiten, 8 Bilder, 1 Tabelle, 33 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Pitting corrosion and crevice corrosion behaviors of high nitrogen austenitic stainless steels

    Li, H. b. / Jiang, Z. h. / Yang, Y. et al. | British Library Conference Proceedings | 2009


    Nitrogen-bearing stainless steels: cost-effective materials for seawater service

    Latha, G. / Rajendran, N. / Rajeswari, S. | Tema Archiv | 1998


    Corrosion behavior of steels in Gulf seawater environment

    Malik, A.U. / Ahmad, S. / Andijani, I. et al. | Tema Archiv | 1999


    Corrosion behavior of some highly alloyed stainless steels in seawater

    Malik, A.U. / Siddiqi, N.A. / Andijani, I.N. | Tema Archiv | 1994