The feasibility has been studied of producing fillet welds in lap joints in Alloy 5182 aluminum sheet with a high-power diode laser. Laser energy absorption and bead formation were found to be very sensitive to surface conditions. Sanding and cleaning of workpieces reduced the weld area significantly compared to as-received sheet surface conditions. Cleaning, however, reduced oxide tail defects and consistently produced welds with increased throat. The addition of dark substances to the surface of the sheets was shown to increase absorptivity, although not necessarily increasing the weld throat. Effects of laser beam presentation were studied, and operating ranges were defined. Mechanisms of pool development in fillet welds in lap joints were explored. It was found that production of fillet welds lap joints in aluminum sheet with the diode laser is feasible for industrial use and may be especially useful for welding of hem joints in automotive closure panels.
Welding aluminum sheet using a high-power diode laser
Welding Journal, New York ; 85 , 5 ; 101s-110s
2006
10 Seiten, 17 Bilder, 24 Quellen
Aufsatz (Zeitschrift)
Englisch
High power CO2 laser aluminum tailored blank welding
Kraftfahrwesen | 1999
|High Power CO2 Laser Aluminum Tailored Blank Welding
SAE Technical Papers | 1999
|High-power diode laser welding of metal catalytic coverters [4831-10]
British Library Conference Proceedings | 2003
|