The hot deformability of 2519 aluminium alloy under elevated temperatures was studied by the analysis of true stress strain curves and observation of the deformed microstructures with an optical microscope (OM) and a transmission electron microscope (TEM). Compression tests were performed on a Gleeble-1500 thermal simulator at the deformation temperature range from 300 degrees Celcius to 500 degrees Celcius and at a strain rate range of 0.05 s(exp-1). The experimental results showed that the flow stress of 2519 aluminium alloy increases with increasing strain and tends to be constant after a peak at lower strain rates of (epsilon < 25 s(exp-1)), and a dynamic recovered substructure was observed with TEM. The flow stress sawtooth pattern fluctuated and decreased after a peak value with increasing strain and higher strain rates of (epsilon > = 25 s-1), which was associated with a dynamic recrystallization revealed by OM and TEM. Flow softening was due to dynamic precipitate coalescence and not to dynamic recrystallization at elevated temperature and lower strain rate. A hyperbolic sine relationship correlated well for fitting the flow stress as a function of strain rate, and an Arrhenius relationship related temperature and time of dynamic recrystallization. The flow stress of 2519 aluminium alloy during high temperature deformation and time of dynamic recrystallization can be determined from the Zener-Hollomon parameter including the hot deformatioon acitivation energy of 2519 aluminium alloy, which was calculated to be 167,81 KJ/mol from the Arrhenius equation.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    A study on the hot deformability of 2519 aluminum alloy at elevated temperatures


    Beteiligte:
    Lin, Qiquan (Autor:in) / Peng, Dashu (Autor:in) / Li, Yingming (Autor:in) / Lin, Gaoyong (Autor:in)

    Erschienen in:

    Light Metal Age ; 65 , 5 ; 46-49


    Erscheinungsdatum :

    2007


    Format / Umfang :

    4 Seiten, 6 Bilder, 9 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Aluminum alloy 2519 in military vehicles

    Fisher, J.J. jun. / Kramer, L.S. / Pickens, J.R. | Tema Archiv | 2002


    Nr. 2519

    DataCite | 1893


    Stress-corrosion cracking susceptibility of various product forms of aluminum alloy 2519

    Kramer, L.S. / Blair, T.P. / Blough, S.D. et al. | Tema Archiv | 2002


    Hot Deformation Behavior of 2519 Al Alloy during Isothermal Compression

    Li, H. Z. / Zhang, X. M. / Chen, M. G. et al. | British Library Conference Proceedings | 2007


    The Effects of Thermo-Mechanical Treatment on the Properties of 2519 Aluminium Alloy

    Lin, G. Y. / Zhang, Z. F. / Lin, Q. Q. et al. | British Library Conference Proceedings | 2007