Steel structures immersed in seawater are protected from corrosion using cathodic protection systems (sacrificial anodes or impressed current), by paint coatings or by duplex systems in which cathodic protection hinders corrosion at coating's failure sites. The main problem related to those duplex systems is how to avoid cathodic delamination due to the alkalinity generated at cathodic sites. The present paper analyses the effectiveness of red mud suspensions as pre-treatment to avoid cathodic delamination. The study was conducted using mainly electrochemical impedance spectroscopy (EIS). The evolution of the electrode potential with immersion time was also recorded because it concerns the practical aspect of current density necessary to reach the protection potential. The study shows that red mud pre-treatments are effective in avoiding coating's delamination.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Surface treatment of carbon steel substrates to prevent cathodic delamination


    Weitere Titelangaben:

    Oberflächenbehandlung von Kohlenstoffstahl zum Schutz vor kathodischer Schichtablösung


    Beteiligte:
    Collazo, A. (Autor:in) / Izquierdo, M. (Autor:in) / Novoa, X.R. (Autor:in) / Perez, C. (Autor:in)


    Erscheinungsdatum :

    2007


    Format / Umfang :

    6 Seiten, 8 Bilder, 22 Quellen




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch






    Investigating the role of key ingredients on cathodic delamination resistance of high-build pigmented epoxy coatings

    Balaji, R. / Gadhave, K. / Shreepathi, S. et al. | British Library Online Contents | 2013



    Some Observations of Indentation Induced Delamination of Thin Films on Substrates

    Swain, M. V. / Institution of Engineers, Australia / Royal Aeronautical Society; Australian Division | British Library Conference Proceedings | 1993