This paper presents the results of testing and modeling studies on the remaining fatigue life of aircraft wing skins containing natural exfoliation corrosion. Dogbone specimens were manufactured from 7075-T6511 upper wing panels containing natural exfoliation. The maximum depth of the exfoliation damage was determined by an ultrasonic non-destructive inspection (NDI). Fatigue tests were carried out under fully reversed constant amplitude loading (R = -1.0), and fractographic analyses were performed to examine the cracking mechanisms in the exfoliation region. Based on the test findings, a simplified fatigue model was developed to estimate the remaining fatigue life of the corroded specimens. In this model, the exfoliation damage was assumed as a surface crack with a depth that was presumably available from an NDI or grindout database. The comparison indicates that the simplified model gave a good estimation for the remaining fatigue life of the naturally exfoliated specimens.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fatigue modeling for aircraft structures containing natural exfoliation corrosion


    Beteiligte:
    Liao, M. (Autor:in) / Renaud, G. (Autor:in) / Bellinger, N.C. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2007


    Format / Umfang :

    10 Seiten, 26 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Modeling the effects of prior exfoliation corrosion on fatigue life of aircraft wing skins

    Liao Min / Bellinger, N.C. / Komorowski, J.P. | Tema Archiv | 2003


    Ageing aircraft - exfoliation corrosion detection and removal - Search Peening

    Thompson, E. R. / Institution of Mechanical Engineers; Aerospace Industries Division / Royal Aeronautical Society | British Library Conference Proceedings | 1996


    Aircraft structures reliability under corrosion fatigue

    Shi, Pan / Mahadevan, Sankaran | AIAA | 2001


    Modelling of Fatigue Crack Growth from exfoliation and Pitting Corrosion

    Clark, G. / Sharp, P. K. / Mills, T. et al. | British Library Conference Proceedings | 2002