In the present investigation, two different wires for hyperbaric (underwater) GTA (gas tungsten arc) welding of X70 pipelines have been tested with respect to their weld metal mechanical properties. Welding of full coupons at different pressures (seawater depths of 16, 75 and 200 msw) was done with subsequent weld metal chemical analyses, hardness measurements, tensile testing and Charpy V notch testing as well as microstructure characterization. It is shown that both wires satisfied strength requirements set to X70 grade, representing a weld metal overmatch situation. Both wires gave sufficient impact toughness, but the toughness of the Ni-Mo containing weld was reduced with increasing seawater depth. This observation was strongly linked to the positioning of the Charpy V notch, and crack growth in a brittle, partially transformed region as a consequence of reheating by subsequent stringer beads. The embrittling microstructure consisted of high carbon MA (martensite-austenite constituents islands) decorating prior austenite grain boundaries. This microstructure was less pronounced when welding with the high Ni wire, which may explain why no similar toughness drop was found.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Weld metal mechanical properties in hyperbaric GTAW of X70 pipeline


    Weitere Titelangaben:

    Mechanische Schweißmetalleigenschaften beim Unterwasser-Wolfram-Inertgasschweißen einer Rohrleitung aus Stahl X70


    Beteiligte:
    Akselsen, Odd M. (Autor:in) / Fostervoll, Hans (Autor:in) / Harsvaer, Ansgar (Autor:in) / Aune, Ragnhild (Autor:in)


    Erscheinungsdatum :

    2006


    Format / Umfang :

    8 Seiten, 4 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Root bead profiles in hyperbaric GTAW of X70 pipeline

    Akselsen, Odd M. / Harsvaer, Ansgar / Fostervoll, Hans et al. | Tema Archiv | 2006


    Weld joint properties at hyperbaric MIG/MAG welding

    Mueller, L. / Terlinde, G. / Schwalbe, K.H. | Tema Archiv | 1986


    Custom weld metal for arctic pipeline

    Harris, R.A. | Tema Archiv | 2000