Permanganate coatings show promise as replacements for chromate conversion coatings on aluminum alloys used in the aerospace industry. The development of permanganate conversion coatings on AA2024-T3 (UNS A92024) from acid solution was followed for up to 240 s using scanning electron microscopy (SEM), x-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES), and Rutherford backscattering spectroscopy (RBS). The permanganate coatings have a manganese dioxide (MnO2)-rich exterior surface covering a mixed Al-Mn oxide with a composition close to MnO2-Al2O3. RBS and AES depth profiles indicate that Mn is distributed throughout the oxide over the metal matrix, while XPS confirmed that Mn(IV) and Al(III) were both present in the coating. The onset of coating formation from permanganate solutions is rapid (<30 s) with the maximum thickness (50 nm to 70 nm) being reached after approximately 60 s. The limit on coating thickness may be due to the passivation of boehmite (AlOOH) by MnO2. Increased deoxidation time prior to coating had little effect on the final coating thickness, but did increase the degree of manganese incorporation.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Development of permanganate-based coatings on aluminum alloy 2024-T3


    Weitere Titelangaben:

    Entwicklung von Schichten auf Permanganatbasis für die Aluminiumlegierung 2024-T3


    Beteiligte:
    Hughes, A.E. (Autor:in) / Gorman, J.D. (Autor:in) / Harvey, T.G. (Autor:in) / Galassi, A. (Autor:in) / McAdam, G. (Autor:in)

    Erschienen in:

    Corrosion, Houston ; 62 , 9 ; 773-780


    Erscheinungsdatum :

    2006


    Format / Umfang :

    8 Seiten, 9 Bilder, 2 Tabellen, 15 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Corrosion behavior of 2024 aluminum alloy anodized in presence of permanganate and phosphate ions

    Mohammadi, M. / Yazdani, A. / Bahrololoom, M. E. et al. | British Library Online Contents | 2013


    Aluminum Alloy 2024, Plate and Sheet

    SAE Technical Papers | 2015


    Creep Resistance of 2024 Aluminum Alloy

    Tsai, Chih-Jrn / Wang, Le-Min / National Defense Univ. | SAE Technical Papers | 2013