Hydrogen permeation through API 5L X65 pipeline steel was studied under freely corroding conditions in (a) 5% NaCl + 0.5% acetic acid and (b) 1 N H2SO4 + 10 mg/l sodium arsenite. A steady state condition with regards to permeation flux is not obtained due to the presence of corrosion product, changing sample dimension and a possible change in hydrogen availability on the corroding surface. A unique way of calculating the sub-surface hydrogen concentration (C0) under non-steady state freely corroding conditions has been developed. The C0 has been evaluated as a function of exposure time in (a) and (b) solution. The sub-surface hydrogen concentration (C0) increased initially but then decreased with increasing exposure to the corroding solutions, after demonstrating an early maximum. The changes in C0 have been explained taking into consideration the corrosion products that developed, the possible anodic reactions, the changes in sample thickness and other issues in the dynamic system.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Hydrogen entry into pipeline steel under freely corroding conditions in two corroding media


    Weitere Titelangaben:

    Wasserstoffaufnahme von Rohrstahl bei freier Korrosion in zwei Korrosionsmedien


    Beteiligte:
    Dey, S. (Autor:in) / Mandhyan, A.K. (Autor:in) / Sondhi, S.K. (Autor:in) / Chattoraj, I. (Autor:in)

    Erschienen in:

    Corrosion Science ; 48 , 9 ; 2676-2688


    Erscheinungsdatum :

    2006


    Format / Umfang :

    13 Seiten, 10 Bilder, 1 Tabelle, 12 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Reliability-based method assesses corroding oil pipeline. Pipeline inspection - conclusion

    Caleyo, F. / Hallen, J.M. / Gonzalez, J.L. et al. | Tema Archiv | 2003


    Reliability-based method assesses corroding pipelines. Pipeline inspection - 1

    Caleyo, F. / Hallen, J.M. / Gonzalez, J.L. et al. | Tema Archiv | 2003


    System reliability of corroding pipelines

    Zhou, Wenxing | Tema Archiv | 2010


    Reliability Assessment of Corroding Ship Hull Structure

    Akpan, Unyime O. | Online Contents | 2003


    The application of gray relational analysis in corroding amorphous Ni alloys

    Yu, L.-p. / Li, J.-y. / Liu, R.-s. | British Library Online Contents | 2002