Short crack fatigue behaviour of a metal inert gas (MIG) welded 2024-T351 aluminium alloy has been studied in terms of crack initiation and propagation, and the microstructural features of the weld. Extensive crack initiation was noted within the weld fusion zone. Relatively small interdentritic defects are seen to be more damaging (in initiating cracks) than the larger gas bubble defects that exist in this region. Cracks were also seen to initiate within the weld heat affected zone where tensile residual stresses were found to be high, however, rapid crack growth and coalescence within the fusion zone is seen to dominate failure. Multiple crack interactions are seen to have a significant effect on failure up to relatively large crack lengths (of the order of the fusion zone width), enhancing the variability in short crack growth. Secondary electron and back-scattered electron imaging, in association with electron back-scattered diffraction (EBSD) mapping, were carried out on failed samples to assess the associated microstructural interactions.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Micromechanical aspects of fatigue in a MIG welded aluminium airframe alloy. Part 2 Short fatigue crack behaviour


    Beteiligte:
    Lefebvre, Fabien (Autor:in) / Sinclair, I. (Autor:in)


    Erscheinungsdatum :

    2005


    Format / Umfang :

    8 Seiten, 22 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch





    Fatigue and Fracture Behaviour of Friction Stir Welded Aluminium Alloy AA6056-T6

    Vaidya, W. V. / Angamuthu, K. / Ventzke, V. et al. | British Library Conference Proceedings | 2004


    Outlook on airframe fatigue

    Tye, W. | Engineering Index Backfile | 1955


    Outlook on airframe fatigue

    Tye, W. | Engineering Index Backfile | 1955


    Outlook on airframe fatigue

    Tye, W. | Engineering Index Backfile | 1955