Type I and II hot corrosion attack has been observed on certain marine gas turbine engines in the area of the first stage turbine hardware. In order to improve the service life and resistance to Type II hot corrosion of these turbine blades, laboratory testing of the current, baseline coating and several candidate replacement coatings was initiated using a low-velocity, atmospheric-pressure burner-rig (LVBR). During a recent high-temperature work, it was discovered that high-temperature coatings on various superalloy substrates behaved differently during 1000 hours of exposure in a Type I hot corrosion environment at 1650 deg F (899 deg C). Differences in chemical compositions between a coating and a substrate alloy can lead to interdiffusion between these materials that can modify the oxidation and corrosion resistance of the coating and the mechanical properties of the coating-substrate system. The stress state may also significantly influence and increase the magnitude of the interdiffusion that may lead to deleterious precipitation reactions. The crystal orientation or alloy phase of the substrate may also contribute to interdiffusion rates. The paper examines the chemistries of two high-temperature coatings applied on two different superalloy substrates prior to LVBR testing and their respective interactive effects on hot corrosion resistance after exposure to a hot corrosion environment. These interactions include resultant changes in the chemistries of the coatings and the alloy substrates and possible phase transformations.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Substrate-coating interactions and their effects on hot corrosion resistance


    Beteiligte:


    Erscheinungsdatum :

    2004


    Format / Umfang :

    12 Seiten, 5 Bilder, 3 Tabellen, 22 Quellen




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    CORROSION PREVENTION COATING AND SUBSTRATE

    ZHU TIANLI / ZHANG WEILONG / MICHAEL A KRYZMAN et al. | Europäisches Patentamt | 2020

    Freier Zugriff

    Effects of Silicone Coating on Corrosion Resistance of Aluminized Steel Sheets for Automotive Mufflers

    Fukumoto, H. / Taomoto, T. / Sugawara, H. et al. | British Library Conference Proceedings | 1992


    Corrosion resistance improvement of brazed evaporator by surface coating development

    Casenave,C. / Philippe,M. / Laronde,R. et al. | Kraftfahrwesen | 2014