The electrochemical behavior of microalloyed steel under H2S environment at room temperature and at 55 deg C suggests that the superficial degradation in this steel is due to the combination of several mechanisms in which uniform corrosion plays a less relevant role, while localized corrosion and diffusion control (where diffusion of species such as H2S, HS(-) is possible) are key mechanism for the corrosion process of this steel. It also was found that the limiting current (il increases proportionally with increase in temperature, leaving clear evidence for the existence of diffusion control. The estimation of corrosion rates by means of Rp technique, taking into account the diffusion control shows that, at room temperature, steel 2 presents the lowest corrosion rate with respect to steel 1. This behavior is reversed at 55 deg C, steel 2 being more susceptible to corrosion.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Electrochemical study of two microalloyed pipeline steels in H2S environments


    Beteiligte:
    Fragiel, A. (Autor:in) / Serna, S. (Autor:in) / Perez, R. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2005


    Format / Umfang :

    7 Seiten, 6 Bilder, 4 Tabellen, 10 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Crack growth in microalloyed pipeline steels for sour gas transport

    Serna, S. / Campillo, B. / Albarran, J.L. | Tema Archiv | 2005


    Microalloyed high-strength steels

    Olsson, Kennet / Gladh, Magnus / Hedi, Jan-Erik et al. | Tema Archiv | 2006



    Fatigue of Microalloyed Bar Steels

    Matlock, David K. / Krauss, George / Johnson, John A. | SAE Technical Papers | 2000


    Fatigue of microalloyed bar steels

    Johnson,J.A. / Krauss,G. / Matlock,D.K. et al. | Kraftfahrwesen | 2000