The corrosion of copper in 1 M NaCl has been investigated at room temperature and at 80 deg C by an on-line resistance probe, solution analysis of dissolved copper and weight loss measurements. At room temperature, corrosion of the copper as indicated by an increase of the probe resistance has been detected during the first 60-80 h of exposure. After the corrosion potential has reached the immunity region of Cu, a decrease in the resistance of the sensor is observed, probably due to redeposition of Cu from the solution. It can be concluded that the corrosion of copper at room temperature virtually stops after 60-80 h due to the anoxic conditions established in the experiments. The similarity in the trends of the corrosion and redox potential during exposure seems to indicate that Cu(II) contained in the native oxide on Cu and/or formed by homogeneous oxidation of Cu(I) during the initial oxic period of exposure acts as a redox-agent determining the chemical conditions in the closed system.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Corrosion of copper in 1 M NaCl under strictly anoxic conditions


    Beteiligte:
    Bojinov, Martin (Autor:in) / Laitinen, Timo (Autor:in) / Mäkelä, Kari (Autor:in) / Snellman, Margit (Autor:in) / Werme, Lars (Autor:in)


    Erscheinungsdatum :

    2004


    Format / Umfang :

    6 Seiten, 4 Bilder, 9 Quellen




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Photochemical synthesis of biomolecules under anoxic conditions

    Folsome, Clair / Brittain, Andrew / Zelko, Michael | Online Contents | 1983




    NaCl-induced hot corrosion of stainless steels

    Shianta, Y. / Hashiura, K. / Takahashi, F. | Tema Archiv | 1987