The fracture of a wheel tire which had brought about the accident of Eschede clearly was caused by a fatigue crack at a relatively low mean stress level. The final fracture only occurred after the remaining cross-section had dropped to about 20%. The material corresponded to all specifications; no traces or pre-existing flaws which could have initiated a fatigue crack could be detected. Service loads had never been determined for this type of wheel, train and track. Before the wheel was commissioned there were performed strain measurements on a prototype of the wheel, fatigue tests on complete wheels and extended service tests on rail tracks. This procedure corresponded to the UIC-recommendations in force at that time. Seen from todays view-point facilities for design would be better. For this type of rubber-sprung wheel no individual UIC-guideline existed. After the accident fatigue tests have been carried out on whole wheels and on segments of tires which gave as result that a fatigue load of nearly four times the nominal wheel load would have been necessary to produce a fatigue crack without pre-existing flaw, which is practically impossible because the tire comes into contact with the wheel disc already at wheel loads of 2-2.5-times the nominal wheel load. When the segments were tested, a fatigue crack could be produced only with an initial flaw at least nearly 1 mm deep and a load 2.5-times the nominal load, without notch only at about 7 times the nominal load. Since no pre-existing flaw at all had been found at the crack origin, the fatigue crack must have started from other reasons.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The railway accident of Eschede - technical background


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    2004


    Format / Umfang :

    21 Seiten, 26 Bilder, 12 Tabellen, 9 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Eschede ... Eschede : mit der Bahn ins Industriezeitalter

    Seebo, Kurt-Werner | GWLB - Gottfried Wilhelm Leibniz Bibliothek | 1992


    Eschede ... Eschede : mit der Bahn ins Industriezeitalter

    Seebo, Kurt-Werner | GWLB - Gottfried Wilhelm Leibniz Bibliothek | 1987


    Eschede Kalastrophe

    Online Contents | 1998



    Eschede crash

    Online Contents | 1998