Modification of graphite for anode of lithium ion batteries is investigated. Results of X-ray diffraction shows lithium and aluminum exists as Li compound (CH3COOLi dot 2H2O) and Al compound (AlD3) in the graphite, respectively. The Brunauer-Emmer-Teller (BET) surface area of the modified graphite increases. According to the electrochemical measurements of Li/C cell and prototype Li-ion batteries, the Li-doped graphite has large reversible capacity of 312.2 mA dot h/g, low irreversible capacity of 52.9 mA dot h/g, and high initial coulombic efficiency of 85.51%. The 063448 size prototype battery with Li-doped graphite anode has large discharge capacity of 845 mA dot h and good cycling performance. The initial charge/discharge characteristic of Al-doped graphite is close to those of undoped graphite, but the prototype battery with Al-doped anode shows the best cycling performance with capacity retention ratio of 94.06% at the 200th cycle.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of lithium or aluminum substitution on the characteristics of graphite for anode of lithium ion batteries


    Beteiligte:
    Guo, Huajun (Autor:in) / Li, Xinhai (Autor:in) / Wang, Zhixing (Autor:in) / Peng, Wenjie (Autor:in) / Guo, Yongxing (Autor:in)

    Erschienen in:

    Rare Metals ; 22 , 4 ; 280-284


    Erscheinungsdatum :

    2003