Results of studies concerning the productive weld joints in high-strength low-alloy steels made at various welding parameters and thickness of plates were presented. Properties of materials in state of delivery and after heat treatment and properties of weld and heat-affected zone were determined. The steel weldments with an increased and high impact resistance were found very sensitive to deterioration under action of thermal cycles with slow cooling. The decrease in the impact resistance was observed also in the original material close to the weld. Formation of martesite-austenite and martensite-austenite-carbide islands was regarded to the local segregation of the carbon. Presence of the islands was observed also in simulated heat-affected zones. (New Materials and New Technologies in Shipbuilding and Engineering Industry, 2nd Polish Conference, Miedzyzdroje, PL, Sep 7-10, 2003)


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Problemy spawania stali o duzej wytrzymalosci na konstrukcje okretowe


    Weitere Titelangaben:

    Problems connected with welding a high-strength steel used in shipping construction


    Beteiligte:
    Mroczka, K. (Autor:in) / Tasak, E. (Autor:in)

    Erschienen in:

    Inzynieria materialowa ; 24 , 6 ; 742-745


    Erscheinungsdatum :

    2003


    Format / Umfang :

    4 Seiten, 10 Bilder, 3 Tabellen, 8 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Polnisch