Water wetting is a crucial issue in carbon dioxide (CO2) corrosion of multiphase flow pipelines made from mild steel. This study demonstrates the use of a novel benchtop apparatus, a horizontal rotating cylinder, to study the effect of water wetting on CO2 corrosion of mild steel in two-phase flow. The setup is similar to a standard rotating cylinder except for its horizontal orientation and the presence of two phases - typically water and oil. The apparatus has been tested by using mass-transfer measurements and CO2 corrosion measurements in single-phase water flow. CO2 corrosion measurements were subsequently performed using a water/hexane mixture with water cuts varying between 5% and 50%. While the metal surface was primarily hydrophilic under stagnant conditions, a variety of dynamic water wetting situations was encountered as the water cut and fluid velocity were altered. Threshold velocities were identified at various water cuts when the surface became oil-wet and corrosion stopped.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Horizontal rotating cylinder - a compact apparatus for studying the effect of water wetting on carbon dioxide corrosion of mild steel


    Weitere Titelangaben:

    Horizontal rotierender Zylinder - Eine kompakte Vorrichtung zur Untersuchung des Einflusses von Wasserbenetzung auf die Kohlendioxidkorrosion von unlegiertem Stahl


    Beteiligte:
    Nesic, S. (Autor:in) / Carroll, F. (Autor:in)

    Erschienen in:

    Corrosion, Houston ; 59 , 12 ; 1085-1095


    Erscheinungsdatum :

    2003


    Format / Umfang :

    11 Seiten, 8 Bilder, 16 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch





    Inhibition of carbon dioxide corrosion of mild steel by imidazolines and their precursors

    Jovancicevic, V. / Ramachandran, S. / Prince, P. | Tema Archiv | 1999



    Ship carbon dioxide steel cylinder lightering trolley

    FU GANG / YANG GUOCHENG / XU FOZHONG et al. | Europäisches Patentamt | 2023

    Freier Zugriff

    Inhibition effect of thioglycolic acid on carbon dioxide corrosion of carbon steel

    Bilkova, K. / Hackerman, N. / Bartos, M. | Tema Archiv | 2004