The objective of this work was to try to desensitize an energetic material by using sol-gel processing and freeze drying to incorporate the energetic material into the fuel matrix on the nano (or at least submicron) particle size scale. Hydrazinium diperchlorate ([N2H6][ClO4]2 or HP2) and resorcinol-formaldehyde (RF) were chosen as the oxidizer and fuel, respectively. Solid loading up to 88% HP2 was achieved by using the sol gel-to-cryogel method. Various weight percentages of HP2 in RF were characterized by elemental analysis, scanning electron (SEM) and optical microscopy, T-jump/FTIR spectroscopy, DSC, and drop-weight impact. SEM indicated that 20-50 nm diameter HP2 plates aggregated into porous 400-800 nm size clusters. Below 80% HP2 the cryogels are less sensitive to impact than physical mixtures having the same ratios of HP2 and RF. The decomposition temperatures of the cryogels are higher than that of pure HP2, which is consistent with their lower impact sensitivity. The heat of decomposition as measured at a low heating rate increases with increasing percentage of HP2. The cryogels and physical mixtures release similar amounts of energy, but the cryogels exhibit mainly a single exotherm by DSC whereas the physical mixtures showed a two-step energy release. Flash pyrolysis revealed gaseous product ratios suggestive of more energy being released from the cryogels than the physical mixtures. Cryogels also burn faster by visual observation. (Abstract Copyright [2003], Wiley Periodicals, Inc.)


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Thermal decomposition of energetic materials 85: Cryogels of nanoscale hydrazinium diperchlorate in resorcinol-formaldehyde


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    2003


    Format / Umfang :

    5 Seiten, 7 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Decomposition and flame structure of hydrazinium nitroformate

    Louwers, Jeroen / Parr, Tim / Hanson-Parr, Donna | AIAA | 1999


    Decomposition and Flame Structure of Hydrazinium Nitroformate

    Louwers, J. / Parr, T. / Hanson-Parr, D. et al. | British Library Conference Proceedings | 1999



    Introduction: Nanoscale Composite Energetic Materials

    Steven Son / Richard Yetter / Vigor Yang | AIAA | 2007