The behaviour, in conditions of total immersion, of an acrylic water-based paint applied to a St 35.8 steel, has been studied using electrochemical techniques. The data obtained have enabled a three-step mechanism to be proposed. In the first step, there is an increase in the activity of the system, as a consequence of the entry of water. In the second step, once a critical level in the water content has been passed, the inhibitor pigments are activated, and this leads to a decrease in the electrochemical activity. Finally, once that the pigments have been exhausted, there is a loss of the protective properties of the paint, with the result that the activity detected is similar to that of the bare metal.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Degradation mechanism of an acrylic water-based paint applied to steels


    Beteiligte:
    Bethencourt, M. (Autor:in) / Botana, F.J. (Autor:in) / Cano, M.J. (Autor:in) / Osuna, R.M. (Autor:in) / Marcos, M. (Autor:in)


    Erscheinungsdatum :

    2003


    Format / Umfang :

    5 Seiten, 6 Bilder, 1 Tabelle, 21 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Nanocomposite acrylic paint with self-cleaning action

    Carneiro, C. / Vieira, R. / Mendes, A. l. et al. | British Library Online Contents | 2012


    Paint bake strengthening in water quenched continuously annealed steels

    Gupta,I. / Bhat,S.P. / Chine,R.S. et al. | Kraftfahrwesen | 1984


    Paint Bake Strengthening in Water Quenched Continuously Annealed Steels

    Gupta, Indra / Cline, Richard S. / Bhat, Shrikant P. | SAE Technical Papers | 1984


    Surveyor white paint degradation.

    HAGEMEYER, W. A. | AIAA | 1967


    Surveyor white paint degradation.

    Hagemeyer, W. A., Jr. | NTRS | 1967