External transgranular cracking was observed on underground pipelines. The phenomenon took place under disbonded coating zones and was induced by the presence of diluted bicarbonate aqueous solution containing dissolved carbon dioxide (CO2). The observed environmental-assisted cracking is very often interpreted as a result of the inefficiency of the cathodic protection. However, some recent local electrochemical potential measurements on buried pipeline surfaces displayed important fluctuations with occasional overprotection conditions. The main objective of this work was to investigate the steel surface behavior under open-circuit potential conditions and over a wide range of cathodic potentials to identify the optimum electrochemical conditions to initiate cracking. Low-frequency cyclic loading tests were performed under various electrochemical conditions: underprotection, overprotection, and alternating stages of under- and overprotection. In low-pH simulated groundwater, the X-52 pipeline steel did not display active-passive electrochemical behavior. Significant general dissolution of the ferrite occurred at open-circuit potential whereas an adherent calcium carbonate (CaCO3) deposit appeared at low cathodic overpotentials. Damage caused by hydrogen was observed for elevated overpotentials. Alternating polarization stages, enhancing either material dissolution, deposit formation, or hydrogen entry, seemed to generate the more favorable conditions for crack initiation. Local hydrogen ingress appeared to be the main mechanism for microcrack propagation.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fatigue crack initiation on low-carbon steel pipes in a near-neutral-pH enviroment under potential control conditions


    Weitere Titelangaben:

    Ermüdungsrissinitiierung von kohlenstoffarmen Stahlrohren in pH-neutraler Umgebung unter kontrollierten Potentialbedingungen


    Beteiligte:
    Puiggali, M. (Autor:in) / Rousserie, S. (Autor:in) / Touzet, M. (Autor:in)

    Erschienen in:

    Corrosion, Houston ; 58 , 11 ; 961-970


    Erscheinungsdatum :

    2002


    Format / Umfang :

    10 Seiten, 7 Bilder, 2 Tabellen, 16 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Programming Enviroment of Control Algorithms

    Mota-Martinez, Mizantha Concepsion / Reyes-Cortes, Fernando / Cid-Monjaraz, Jaime | IEEE | 2017


    WATER ENVIROMENT MONITORING SYSTEM

    JUN HYUNG SUK / KIM MOO KUN | Europäisches Patentamt | 2022

    Freier Zugriff

    Multiaxial Fatigue Crack Initiation in Rubber

    Mars, W.V. | Online Contents | 2001


    WATER ENVIROMENT MONITORING SYSTEM

    Europäisches Patentamt | 2023

    Freier Zugriff