The corrosion properties of weld overlays of Ni-based alloys made on 6Mo stainless steels have been investigated using different test methods. Of the different weld overlays tested, only the Alloy 59 types seem to be beneficial with respect to crevice corrosion initiation when compared with 6Mo base material. Both alloy C-22 and Alloy C-276 weld overlays have slightly lower critical crevice temperatures (CCT) while Alloy 625 and C-4 weld overlays have considerably lower CCTs than the 6Mo base material. Applying a test method or using a gasket material giving less critical crevice geometry than PTFE does, increases the critical crevice corrosion temperature considerably. Care must be taken when evaluating results from testing and when specifying test temperature and test method for quality control. A crevice corrosion test method simulating the condition when starting up a chlorinated sea water system has been developed.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Crevice corrosion properties of weld overlays of Ni-based alloys compared to 6Mo stainless steels for sea water applications


    Beteiligte:
    Rogne, T. (Autor:in) / Drugli, J.M. (Autor:in) / Solem, T. (Autor:in) / Salbu, H. (Autor:in) / Skjellevik, H. (Autor:in)


    Erscheinungsdatum :

    2001


    Format / Umfang :

    11 Seiten, 10 Bilder, 3 Tabellen, 8 Quellen



    Medientyp :

    Aufsatz/Kapitel (Buch)


    Format :

    Print


    Sprache :

    Englisch




    Crevice corrosion of nickel base alloys and high-alloy stainless steels in sea water

    Guyader, H. le / Debout, V. / Grolleau, A.M. | Tema Archiv | 2001


    Mechanism of dissimilar metal crevice corrosion of superferritic stainless steels

    Salamat, G. / Juhl, G.A. / Kelly, R.G. | Tema Archiv | 1995


    Pitting corrosion and crevice corrosion behaviors of high nitrogen austenitic stainless steels

    Li, H. b. / Jiang, Z. h. / Yang, Y. et al. | British Library Conference Proceedings | 2009