In order to clarify the significance of corrosion damage for risk assessment, bend tests were carried out on a roughened corroded annular plate prepared from an oil storage tank. It was found that a marked decrease of load carrying capacity occurred in the high deflection region depending upon the degree of corrosion damage. The reason for extensive loss of load carrying capacity was successfully explained from successive observation of crack growth behavior on the corroded surface of the annular plate. Photographic evidence showed that multiple cracks, initiated around individual pits, grew rapidly not only by crack growth, but also by coalescence with other neighboring cracks under the influence of plastic constraint derived from the welded joint. The linking up of multiple cracks leading to a catastrophic failure considered to be a characteristic event of the roughened corroded component, and was expected to occur depending upon the degree of corrosion damage under a complex state.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fracture behavior of a corroded structural component under bending load


    Beteiligte:
    Ohashi, M. (Autor:in) / Yamamoto, H. (Autor:in) / Itoh, Y. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2001


    Format / Umfang :

    16 Seiten, 19 Bilder, 1 Tabelle, 8 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Experimental Study on Bending Behavior of Corroded Post-Tensioned Concrete Beams

    Zeng, Y.H. / Huang, Q.H. / Gu, X.L. et al. | British Library Conference Proceedings | 2010


    Elastic-plastic fracture analysis of stiffened plate under bending load

    Wang, Hong / Yang, Ping / Deng, Jun-lin et al. | IEEE | 2015


    Experimental assessment of corroded steel box-girders subjected to uniform bending

    Saad-Eldeen, S. / Garbatov, Y. / Guedes Soares, C. | Taylor & Francis Verlag | 2013


    The failure mechanism analysis of corroded pipelines repaired with CFRP under bending loads using FEM

    Peng, Zhang / Yu, Zhang / Jianhang, Xin et al. | Taylor & Francis Verlag | 2024