The UNS N08367 (AL-6XN(registered trademark)) alloy was designed to be a seawater resistant alloy and has been successfully used in a multitude of marine and offshore applications including process piping systems, heat exchanger equipment, drilling platforms, and desalination systems. Although the N08367 alloy has improved resistance to chloride stress corrosion cracking (CSCC) it is not completely immune to this mode of failure. This investigation exposed U-bend specimens to various chloride bearing solutions to better define cracking threshold of the N08367 alloy. Samples were exposed in an autoclave using static solutions and no effort was made to either aerate or dearate test solutions. Measurements in solutions with chloride concentrations of 0.02 to 2.0 wt% mixed from ASTM D-1141-52 sea salt, readily produced cracking at temperatures of 260 degree C. The threshold temperature for the onset CSCC in straight NaCl solutions was found to increase as the chloride concentration decreased. In the range of 0.02 to 15.8 wt% chlorides the threshold temperature in degree C for the onset of cracking can be defined as follows. TSCC = 190.05 - 47.42log (Cl). The results of this testing indicate that it is unlikely to stress corrosion crack this alloy in presence of chlorides at temperatures in the range of atmospheric boiling (approximately = 100 degree C). At temperatures greater than 120 degree C cracking can be initiated depending on the chloride content of the environment.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Chloride stress corrosion cracking resistance of 6% Mo stainless steel alloy (UNS N08367)


    Beteiligte:
    Fritz, J.D. (Autor:in) / Gerlock, R.J. (Autor:in)

    Erschienen in:

    Desalination ; 135 , 1-3 ; 93-97


    Erscheinungsdatum :

    2001


    Format / Umfang :

    5 Seiten, 8 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch








    Stress corrosion cracking of the AlZn5Mg1 alloy

    Jawan, H. A. / Labanowski, J. / Zielinskia, A. et al. | British Library Conference Proceedings | 1995