Fatigue loading is a significant factor in determining the service life of the marine concrete structures, as it considerably enhances the deterioration process in a corrosive marine environment. To evaluate the durability of marine concrete structures subjected to fatigue loading, accelerated laboratory testing was carried out on full- and half-size reinforced concrete specimens, subjected to static and fatigue loading with three different water cement ratios (w/c=0.3, 0.4, and 0.6). The marine tidal zone was simulated by alternate filling and draining of the tank, and a galvanostatic corrosion technique was used to accelerate corrosion of the reinforcement. Half-cell potential measurements and crack investigations were followed by ultimate strength testing. The significant findings include the adverse effect of fatigue loading, existence of an explicit size effect, and the negative effect of increasing water/cement ratio.
Galvanostatic testing for the durability of marine concrete under fatigue loading
Cement and Concrete Research ; 31 , 3 ; 343-349
2001
7 Seiten, 7 Quellen
Aufsatz (Zeitschrift)
Englisch
Durability of Tapered Composite Laminates under Static and Fatigue Loading
British Library Conference Proceedings | 2011
|Durability Analysis Under Complex Multiaxial Loading
SAE Technical Papers | 1987
|First-principles thermal modeling of hybrid pseudocapacitors under galvanostatic cycling
Online Contents | 2016
|Modeling of Chloride Ion Diffusion in Concrete under Fatigue Loading
Online Contents | 2019
|