In this study, the failure modes of cartwheel and mechanical properties of materials have been analyzed. The results show that rim cracking is always initiated from stringer-type alumina cluster and driven by a combination effect of mechanical and thermal load. The strength, toughness, and ductility are mainly determined by the carbon content of wheel steels. The fatigue crack growth resistance is insensitive to composition and microstructure, while the fatigue crack initiation life increases with the decrease of austenitic grain size and pearlite colony size. The dynamic fracture toughness, KID, is obviously lower than static fracture toughness, KIC, and has the same trend as KIC. The ratio of KID/sigmaYD is the most reasonable parameter to evaluate the fracture resistance of wheel steels with different composition and yield strength. Decreasing carbon content is beneficial to the performance of cartwheel.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Failure modes and materials performance of railway wheels


    Beteiligte:
    Liu, Z.X. (Autor:in) / Gu, H.C. (Autor:in)


    Erscheinungsdatum :

    2000


    Format / Umfang :

    5 Seiten, 13 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Machining railway wheels

    Engineering Index Backfile | 1940


    Micrometer for railway wheels

    Engineering Index Backfile | 1942


    Railway wheels and axles

    Sanders, T.H. | Engineering Index Backfile | 1920


    STEEL FOR PRODUCING RAILWAY WHEELS

    BEZOBRAZOV YURIY ALEKSEEVICH / BROYTMAN OLEG ARKADIEVICH / TERENTIEV MAKSIM IGOREVICH et al. | Europäisches Patentamt | 2019

    Freier Zugriff

    RAILWAY VEHICLE WHEELS CONDITION DIAGNOSTICS

    KAEMPFER BJOERN / WEBER FRANZ-JOSEF | Europäisches Patentamt | 2019

    Freier Zugriff