Reliability enhancement of thick Al wire bonds during thermal fatigue test has been investigated from a metallurgical viewpoint. Al wire bonds degrade with the increase of crack length during thermal fatigue tests with high Delta Tj due to the tensile stress generated by the thermal expansion coefficient mismatch between Al wires and Si. It is also found that cracks propagate along the small grain boundaries of Al wires at the bonding interface. It is predicted that the Al wire bonds may not degrade due to thermal fatigue if Delta Tj is controlled below 40 K, i.e., keeping it within the actual temperature fluctuation range in IGBT modules for traction motor drives. The reliability of Al wire bonds can be enhanced by increasing the grain size of the Al wire at the bonding interface. The high temperature bonding is considered to be a good candidate for enhancing the reliability of Al wire bonds.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Reliability of thick Al wire bonds in IGBT modules for traction motor drives


    Beteiligte:
    Onuki, J. (Autor:in) / Koizumi, M. (Autor:in) / Suwa, M. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2000


    Format / Umfang :

    5 Seiten, 11 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Reliability of IGBT Power Modules for Traction Applications

    Wolfgang, E. / Franke, T. / Laska, B. et al. | British Library Conference Proceedings | 1999



    GTO and IGBT traction three phase inverter drives

    White, R.D. | IET Digital Library Archive | 1998


    Direct-Soldered Mounting Inverter Modules for Traction Motor Drives†*

    Konrad, Charles E. (Bud) / Lai, Jih-Sheng (Jason) / Kim, Junhyung | SAE Technical Papers | 2002


    Direct-soldered mounting inverter modules for traction motor drives

    Lai,J.S. / Kim,J. / Konrad,C.E. et al. | Kraftfahrwesen | 2002