As composite materials find increased use in infrastructure applications, where design lives are typically much longer than those in aerospace, the issue of durability becomes more critical. The tolerance of composites to damage induced by cyclic loading and moisture ingress is of utmost importance. This study highlights the effects of short-term cyclic moisture aging on the strength and fatigue performance of a glass/vinyl ester pultruded composite system. In particular, it addresses the change in quasi-static properties and tension-tension (R = 0.1) fatigue behavior of a commercial glass/vinyl ester system in fresh and salt water. The quasi-static tensile strength was seen to reduce by 24% at a moisture concentration of 1% by weight. This reduction in strength was not recoverable even when the material was dried, suggesting that the exposure to moisture caused permanent damage in the material system. Even though the fatigue damage process of the unaged or 'as-delivered', fresh-water- and salt-water-saturated material was similar, the cyclic moisture absorption-desorption experiments altered the fatigue performance of the composite system tested. Results were consistent with Mandell's postulate that fatigue failure in glass-fiber-reinforced polymeric composites is a fiber-dominated mechanism with a characteristic slope of 10% UTS/decade.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Characterization of fatigue and combined environment on durability performance of glass/vinyl ester composite for infrastructure applications


    Beteiligte:
    McBagonluri, F. (Autor:in) / Garcia, K. (Autor:in) / Hayes, M. (Autor:in) / Verghese, K.N.E. (Autor:in) / Lesko, J.J. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2000


    Format / Umfang :

    12 Seiten, 18 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Flexural fatigue response of repaired S2-glass/vinyl ester composites

    Vaidya, U.K. / Basappa, G. / Mathew, B. et al. | Tema Archiv | 2000


    Fire Protection of Glass/Vinyl Ester Composites for Structural Applications

    Sorathia, U. / Beck, C. / SAMPE | British Library Conference Proceedings | 1996


    Material property characterization of glass and carbon/vinyl ester composites

    Swaminathan, Gowthaman / Shivakumar, Kunigal N. / Sharpe, Mathew | Tema Archiv | 2006