The outer layer of Teflon fluorinated ethylene propylene (FEP) multi-layer insulation (MLI) on the Hubble Space Telescope (HST) was observed to be significantly cracked at the time of the Second HST Servicing Mission (SM2), 6.8 years after HST was launched into low Earth orbit (LEO). Comparatively minor embrittlement and cracking were also observed in FEP materials retrieved from solar-facing surfaces on HST at the time of the First Servicing Mission (3.6 years exposure). After SM2, a Failure Review Board was convened to address the problem of degradation of MLI on HST. In order for this board to determine possible degradation mechanisms, it was necessary to consider all environmental constituents to which the FEP MLI surfaces were exposed. Based on measurements and various models, environmental exposure conditions for FEP surfaces on HST were estimated including: number and temperature ranges of thermal cycles; equivalent sun hours; fluence and absorbed radiation dose of x-rays, trapped protons and electrons, and plasma electrons and protons; and atomic oxygen (AO) fluence. This paper presents the environmental exposure conditions for FEP on the Hubble Space Telescope, briefly describing the possible roles of the environmental factors in the observed FEP embrittlement and providing references to the published works which describe in detail testing and analysis related to FEP degradation on HST.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Environmental exposure conditions for Teflon FEP on the Hubble Space Telescope


    Beteiligte:
    Dever, J.A. (Autor:in) / de Groh, Kim K. (Autor:in) / Banks, B.A. (Autor:in) / Townsend, J.A. (Autor:in) / Barth, J.L. (Autor:in) / Thomson, S. (Autor:in) / Gregory, T. (Autor:in) / Savage, W. (Autor:in)


    Erscheinungsdatum :

    1999


    Format / Umfang :

    15 Seiten, 28 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Analyses of Hubble Space Telescope Aluminized-Teflon Insulation Retrieved After 19 Years of Space Exposure

    Groh, Kim K. / Waters, Deborah L. / Mohammed, Jelila S. et al. | Springer Verlag | 2012


    Degradation of Hubble Space Telescope aluminized-Teflon bi-stem thermal shields

    Groh, Kim K. de / Snyder, Aaron / Finlay, Katherine A. | Tema Archiv | 2008


    Degradation of Hubble Space Telescope metallized Teflon FEP thermal control materials

    Hansen, P.A. / Townsend, J.A. / Yoshikawa, Y. et al. | Tema Archiv | 1998


    Mechanical properties of teflon FEP retrieved from the Hubble space telescope

    Dever, J.A. / Groh, K.K. de / Messer, R.K. et al. | Tema Archiv | 2001


    Mechanical properties degradation of Teflon FEP returned from the Hubble Space Telescope

    Dever, Joyce / de Groh, Kim / Townsend, Jacqueline et al. | AIAA | 1998