Due to a demand by the aerospace industry, NASA has begun developing the next generation of polyimide foams which will be utilized to reduce vehicle weight for the X-33 Program and Reusable Launch Vehicle (RLV) Program. The research activity at NASA Langley Research Center (LaRC) focuses on developing foam and foam structures which are made from a polyimide using monomeric solutions or salt solutions formed from the reaction of a dianhydride dissolved in a mixture of foaming agents and alkyl alcohols at room temperature. This process can produce polyimide foams with varying properties from a large number of monomers and monomer blends. The specific densities of these foams can range from 0.008 g/cc to 0.32 g/cc. Polyimide foams at densities 0.032 g/cc and 0.08 g/cc were tested for a wide range of physical properties. The foams demonstrated excellent thermal stability at 321 degree C, good thermal conductivity at 25 degree C of 0.0003 W/cm-K, compressive strengths as high as 0.84 MPa at 10% deflection, and a limiting oxygen index of 51%. Thermomechanical cyclic testing was also performed on these materials for 50 cycles at temperatures from -253 degree C to 204 degree C. The foams survived the cyclic testing without debonding or cracking.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    High temperature polyimide foams for aerospace vehicles

    Weiser, E.S. / Johnson, T.F. / Clair, T.L.S. et al. | Tema Archiv | 2002


    Polyimide Foam Insulation Materials for Aerospace Vehicles and Spaceport Applications

    Williams, M. K. / Weiser, E. S. / Fesmire, J. E. et al. | British Library Conference Proceedings | 2004



    Aerospace wiring relies on polyimide film

    Tixhon, J.M. | Tema Archiv | 1983


    HIGH TEMPERATURE LAYERED TILE INSULATION SYSTEM FOR AEROSPACE VEHICLES

    HOENING MICHAEL / HOFFMANN MICHELLE / MOYNIHAN KEVIN et al. | Europäisches Patentamt | 2021

    Freier Zugriff