Because aircraft structures are susceptible to corrosion and fatigue damage, which concentrate at joints, there is a possibilty of interactions between corrosion and fatigue, especially as aircraft becomes older. Of particular concern are the longitudinal lap splices of transport aircraft pressure cabins. The paper reports on the disassembly and investigation of lap splices from several types of transport aircraft. Broadly speaking, the investigation showed that pressure cabin longitudinal lap splices have a corrosion problem or a fatigue problem: severe corrosion does not result in Multiple Site Damage (MSD) fatigue cracking, and MSD is not initiated by corrosion. However, there is evidence of a mild environmental effect on MSD fatigue crack growth. The results are discussed with respect to MSD fatigue modelling and simulation and lap splice fatigue analysis methods.
Corrosion and fatigue assessment of aircraft pressure cabin longitudinal lap splices
1999
34 Seiten, 23 Bilder, 5 Tabellen, 26 Quellen
Aufsatz (Konferenz)
Englisch
Fatigue and corrosion in aircraft pressure cabin lap splices
Tema Archiv | 2001
|Panel splices design and analysis of double bubble intersection in composite pressure cabin
Online Contents | 2013
|Eddy-current detection of pitting corrosion in aircraft lap-splices
Tema Archiv | 1996
|Emerald Group Publishing | 1956
|Aircraft cabin pressure assessment systems and methods
Europäisches Patentamt | 2018
|