Corrosion protection mechanism was investigated on newly developed-metal-finished steel sheets for automobile applications. Such alloying elements to zinc as Ni, Co, Mn, Mg and Al retard oxygen reduction reaction because of their stabilizing effect of Zn(OH2) films, leading to improved corrosion resistance. Wet adhesion of cathodic primed full painted system is governed by alkali-induced dissolution of phosphate and zinc coatings during electrocoating. Fe in coating layer improves wet adhesion because of its high alkali-resistance. Both Fe and Ni have a pore blocking effect on phosphate films, with resultant a superior paint performance. The factors affecting perforation of jointed panels were also discussed.
Corrosion protection fundamentals of metal-finished steel sheets for automotive applications
Grundlagen des Korrosionsschutzes von Stahlblech mit Metallfinish fuer den Automobilbau
1983
10 Seiten, 12 Bilder, 5 Tabellen, 8 Quellen
Aufsatz (Konferenz)
Englisch
Corrosion Protection Fundamentals of Metal-Finished Steel Sheet for Automotive Applications
Kraftfahrwesen | 1983
|Trend of corrosion-resistant precoated steel sheets for automotive applications
Tema Archiv | 1984
|Corrosion behavior of several precoated steel sheets for automotive application
Tema Archiv | 1982
|Advances in automotive steel sheets
Tema Archiv | 1998
|