With improvement of shielding method and prevention of heat dissipation from the surface of the mother metal, the study on the possibility of underwater welding of HT50 and HT60 was undertaken. The results obtained are as follows. With the use of water curtain, surrounding water did not intrude the welds and fluxtuation in welding thermal cycle curve shown in the usual underwater welding was not recognized. With improvement of shielding method under water, the cooling rate was moderated and resembled to that in the air. The method covering the surface of the mother metal with tape was available for prevention of heat dissipation from the surface and moderated the cooling from the side of the bead. The hardness of the weld metal and HAZ decreased with increasing of heat input and showed the qualitative correlation with the cooling rate. The maximum hardness of HT50 was less than 380Hv and would not cause the actual problem. (Wassmann)


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Underwater welding of high tensile strength steel


    Weitere Titelangaben:

    Unterwasserschweissen von hochzugfestem Stahl


    Beteiligte:
    Hamasaki, M. (Autor:in) / Sakakibara, J. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1979


    Format / Umfang :

    6 Seiten, 11 Bilder, 2 Tabellen, 9 Quellen


    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Japanisch




    Underwater Welding of Duplex Stainless Steel

    Labanowski, Jerzy / Fydrych, Dariusz / Rogalski, Grzegorz et al. | Tema Archiv | 2011


    Welding of high strength steel sheet

    Br.Welding Inst.,Coventry,GB | Kraftfahrwesen | 1982


    Development of Ultra-High-Strength Steel Sheets with tensile strength of 980MPa

    Fujita, N. / Nonaka, T. / Taniguchi, H. et al. | British Library Conference Proceedings | 2006


    Development of Ultra-High Strength Steel Sheets with Tensile Strength of 980MPa

    Taniguchi, Hirokazu / Yamazaki, Kazumasa / Goto, Koichi et al. | SAE Technical Papers | 2007


    Development of Ultra-High Strength Steel Sheets with Tensile Strength of 980MPa

    Fujita, N. / Nonaka, T. / Tomokiyo, T. et al. | British Library Conference Proceedings | 2007