Flaws occur in aircraft structures due to material and structural manufacturing and processing operations. The most prevalent sources of cracking in aircraft structures are fastener holes, although cracking does occur at locations other than fastener holes (for example, surface cracks). This paper presents a discussion of the most common types of flaws which exist in aircraft structures and the test data and analytical criteria needed to predict their growth. A number of special analytical and structural considerations are discussed such as small flaws, cold-worked-holes, plasticity effects, failure criteria, and multiple flaw sites. The analytical crack growth and residual strength requirements which must be met as well as the initial flaw sizes and shapes which must be assumed in the Air Force damage tolerance design requirements (MIL-A-83444) are presented. Recently developed stress intensity factor solutions for quarter elliptical corner cracks emanating from various types of fastener holes are presented. Predictions using these current solutions are correlated with other approximate solutions as well as experimental test data. (Se)
Part-through crack problems in aircraft structures
Durchgehende Risse in Flugzeugbauteilen
Part-through crack fatique life prediction. ASTM symp. ; 687 ; 168-194
1979
27 Seiten, 21 Bilder, 1 Tabelle, 15 Quellen
Aufsatz (Konferenz)
Englisch
Crack detection in aircraft structures
Engineering Index Backfile | 1956
|Predicting Fatigue Crack Growth on Aircraft Structures
SAE Technical Papers | 1981
|Radiographic Crack Detectability in Multi-Layer Aircraft Structures
British Library Conference Proceedings | 1993
|Crack Deflection in Al-Li Alloys for Aircraft Structures
British Library Conference Proceedings | 1995
|