The spot welding characteristics of VAN-QN (80), a dual-phase HSLA steel, were examined with regard to the strength and ductility of spot welds under static, impact and cyclic loading and compared to a conventional V-N HSLA steel and SAE 1008 low carbon steel. The maximum tensile shear strength of VAN-QN (80) spot welds was found to be proportional to the thickness and ultimate tensile strength of the base metal. VAN-QN (80) spot welds, therefore, were only slightly lower in strength than those in a conventional 80 Ksi yield strength HSLA steel but up to twice the strength of welds in low carbon steel. Weld ductility was lower for VAN-QN (80) than for low carbon steel but greater than for conventional HSLA steel and increased with material thickness. The impact and fatigue properties of VAN-QN (80) welds were similar to those in conventional HSLA and low carbon steels. (DePo)


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Spot weldability of dual-phase steel


    Weitere Titelangaben:

    Punktschweissbarkeit von hochfestem niedriglegiertem Stahl


    Beteiligte:
    Pollard, B. (Autor:in) / Goodenow, R.H. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1979


    Format / Umfang :

    13 Seiten, 19 Bilder, 3 Tabellen, 10 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Spot weldability of dual-phase steel

    Pollard,B. / Goodenow,R.H. / Jones and Laughlin Steel,US | Kraftfahrwesen | 1979


    Spot Weldability of Dual-Phase Steel

    Pollard, B. / Goodenow, R. H. | SAE Technical Papers | 1979


    Resistance Spot Weldability of Three Metal Stack Dual Phase 600 Hot-dipped Galvanized Steel

    Elliott, Adrian / Joaquin, Armando / Wexler, Arnon et al. | SAE Technical Papers | 2007


    Resistance spot weldability of three metal stack dual phase 600 hot-dipped galvanized steel

    Koganti,R. / Coon,T. / Lalam,S. et al. | Kraftfahrwesen | 2007


    Spot weldability of Galfan

    Kraftfahrwesen | 1989