This investigation was undertaken to evaluate the damage tolerance of typical graphite/epoxy structure to service damage AS/3501 graphite/epoxy I-stifflened panels and honeycomb panels were fabricated and its tolerance to lowvelocity impacts was measured. Three impact treats were investigated; runway stones, a blunt impactor with a tip radius of 0.64 cm (1/4 inch), and a blunt impactor with a tip radius of 2.54 cm (1 inch). Impact parameters were selected that would just cause visual damage. This worked well for the runway stones, but for the tests of the one-inch penetrator on the honeycomb panels visual damage was not easily observed. C-scan damage was, however, easily detectable. Residual strength specimens were cut from the damaged panels and tested. The specimens contained damage at levels of 70, 100, 130 % of the level to cause visual (or C-scan) damage. (DePo)


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Investigation of damage tolerance of graphite/epoxy structures and related design implications


    Weitere Titelangaben:

    Untersuchung der Schadenstoleranz von Graphit-Expoxidharz-Verbundwerkstoffen


    Beteiligte:
    Adsit, N.R. (Autor:in) / Waszczak, J.P. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1976


    Format / Umfang :

    72 Seiten


    Medientyp :

    Report


    Format :

    Print


    Sprache :

    Englisch





    Investigation on Damage Tolerance of Carbon/Epoxy Laminate for Aircraft Structural Design

    Park, Hyun Bum ;Kong, Chang Duk ;Lee, Kyung Sun | Trans Tech Publications | 2011


    Investigation on Damage Tolerance of Carbon/Epoxy Laminate for Aircraft Structural Design

    Park, Hyun-Bum / Kong, Chang-Duk / Lee, Kyung-Sun | Tema Archiv | 2011


    Damage tolerance design of composite structures

    Graesser, D.L. / Tuttle, M.E. | Tema Archiv | 1994


    Damage tolerance design of composite structures

    Graesser, D. / Tuttle, M. | AIAA | 1994