Wrought magnesium alloy AZ31 withWrought magnesium alloy AZ31 a thick section of 20 mm was prepared by squeeze castingSqueeze Casting (SC) and permanent steel mold castingPermanent Steel Mold Casting (PSMC). The yield strength (YS), ultimate yield strength (UTS), elongation (ef), and strain-hardening rate of the cast AZ31 specimens were evaluated by tensile testing. The measured engineering stress versus strain curves showed that the SC AZ31 alloyAZ31 alloy exhibited 62 MPa in YS, 194 MPa in UTS, and 13.8% in ef, while the YS, UTS, and ef of the PSMC AZ31 specimen were only 58, 173 MPa, and 9.9%. The results of the tensile testing evidently showed that the YS, UTS, and ef of the SC AZ31 alloy were 7, 12, and 39% higher than those of the PSMC counterpart. The calculated resilience and tensile toughness indicated that the SC AZ31 was more capable of resisting energy loads in elastic deformation and had an ability to absorb energy during plastic deformationPlastic deformation without fracture than that of the PSMCPermanent Steel Mold Casting AZ31. Also, the analyses of the true stress versus strain curves revealed that, upon the onset of plastic deformationPlastic deformation, the strain-hardening rate of the SC AZ31 sample was 10,000 MPa, which was 25% higher than that (8000 MPa) of the PSMC AZ31 specimen. The obtained mechanical propertiesMechanical Properties showcased the fit of the casting process to wroughtCast/wrought processingmagnesiumMagnesiumAZ31 alloyAZ31 alloy, which was squeeze castingSqueeze Casting. The porosityPorosity measurements of the SCSqueeze Castingand PSMCPermanent Steel Mold Casting showed that the SC AZ31 had a porosity of 1.13%, which was the 57% lower than that (2.66%) of the PSMC AZ31 counterpart. The low porosity level of the SC AZ31 alloy should be somewhat responsible for its high mechanical propertiesMechanical Properties.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Porosity and Mechanical Properties of Squeeze Cast and Permanent Mold Cast Wrought Mg Alloy AZ31


    Weitere Titelangaben:

    The Minerals, Metals & Materials Series


    Beteiligte:
    Leonard, Aeriel (Herausgeber:in) / Barela, Steven (Herausgeber:in) / Neelameggham, Neale R. (Herausgeber:in) / Miller, Victoria M. (Herausgeber:in) / Tolnai, Domonkos (Herausgeber:in) / Dhaif, A. (Autor:in) / Shen, W. (Autor:in) / Hu, H. (Autor:in)

    Kongress:

    TMS Annual Meeting & Exhibition ; 2024 ; Orlando, FL, USA March 03, 2024 - March 07, 2024



    Erscheinungsdatum :

    03.02.2024


    Format / Umfang :

    6 pages





    Medientyp :

    Aufsatz/Kapitel (Buch)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Squeeze Cast Automotive Applications and Squeeze Cast Aluminum Alloy Properties

    Corbit, S. A. / DasGupta, R. / Society of Automotive Engineers | British Library Conference Proceedings | 1999



    Squeeze cast automotive applications and squeeze cast aluminium alloy properties

    Orbit,S.A. / DasGupta,T. / CONTECH Div.,US | Kraftfahrwesen | 1999


    Squeeze cast permanent mold ( SCPM ) processes for automotive aluminum castings

    Gerken,D.T. / Conaty,C.C. / Ogiwara,T. et al. | Kraftfahrwesen | 1998


    Squeeze Cast Permanent Mold (SCPM) Processes for Automotive Aluminum Castings

    Conaty, Craig C. / Gerken, David T. / Ogiwara, Toshio | SAE | 1998