Abstract AA6082 alloy reinforced with TiB2 particles was synthesized through stir casting method to yield the AA6082-5(wt%)TiB2 metal matrix composite. Dry sliding wear behaviour was studied to understand the effect of friction stir processing (FSP) on the composite with the design of experiment software, which was used to plan the experiments and was conducted at 15–50 N applied load and 300–1200 rpm rotational speed. It was compared with the same set experiments performed on the sample without FSP. Experiments were conducted by preparing the samples according to specific dimensions on pin-on-disc tribometer at room temperature. Effect of applied load and rotational speed on the wear or mass loss was plotted. It was observed that the mass loss on both the composites is found to be different. Optical microscopy studies were conducted. Abrasive and adhesive wear mechanisms were observed due to the presence of hard TiB2 reinforcement particles.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of Friction Stir Processing on the Dry Sliding Wear Behaviour of AA6082-5TiB2 Composite


    Beteiligte:


    Erscheinungsdatum :

    2018-12-21


    Format / Umfang :

    7 pages





    Medientyp :

    Aufsatz/Kapitel (Buch)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Investigation on Mechanical Properties of AA6082-AA7075 Friction Stir Welded Dissimilar Aluminum Alloys

    Giridharan, K. / Chakravarthi, G. / Karthick, S. et al. | Springer Verlag | 2020


    Investigation on Mechanical Properties of AA6082-AA7075 Friction Stir Welded Dissimilar Aluminum Alloys

    Giridharan, K. / Chakravarthi, G. / Karthick, S. et al. | TIBKAT | 2021



    Microstructure analysis of AA6082/Si3N4 and AA6082/SiC composites

    Sharma, Deepak / Bhushan, Rajesh Kumar | Emerald Group Publishing | 2021


    Friction and wear behaviour of rolling–sliding steel contacts

    Ramalho, A. / Esteves, M. / Marta, P. | Tema Archiv | 2013