This work analyzed the microstructural and mechanical properties of sintered and hot pressed aluminum alloy AA2014, an aluminum metal matrix composite and an aluminum hybrid metal matrix composite. Sample-1 (AA2014), sample-2 (AA2014 + 5wt% TiB2) and sample-3 (AA2014 + 5 wt% TiB2 + 5 wt% Al2O3) were developed by powder metallurgy. It involves elemental powder mixing and uniaxial green compaction in a 350 MPa universal testing machine followed by sintering in a 550 °C electric muffle furnace for 2 h and hot pressing in a vacuum hot press at nitrogen atmosphere for 2 h at 620 °C. Density assessment, study of microstructure and mechanical characterization were subjected to three samples. For both sintering and hot pressed condition, mechanical and physical properties were analyzed. Samples-1, 2, and 3 display a marginal increase of 1, 1.4 and 1.4% of sintered densities after hot pressing. Sample-1, 2, and 3 porosity were decreased by 15.94, 25 and 22.2% after hot pressing. Improved  mechanical properties due to the transfer of load from the matrix to the two reinforcements TiB2 and Al2O3 after hot pressing.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Microstructural and Mechanical Characterization of Sintered and Hot Pressed Hybrid Metal Matrix Composites


    Weitere Titelangaben:

    Lect.Notes Mechanical Engineering


    Beteiligte:
    Gascoin, Nicolas (Herausgeber:in) / Balasubramanian, E. (Herausgeber:in) / Sundaram, Jayavelu (Autor:in) / Udaya Prakash, J. (Autor:in) / Ramajayam, Mariappan (Autor:in)


    Erscheinungsdatum :

    27.09.2020


    Format / Umfang :

    10 pages





    Medientyp :

    Aufsatz/Kapitel (Buch)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch