Abstract The effect of bonded crack retarders on fatigue crack growth behavior and residual strength of fuselage panels was studied through the tests of 3 baseline panels (JZ-1, JZ-2 and JZ-3) and 3 reinforced panels (SR-1, SR-2 and SR-3). The baseline panels were curved fuselage panels with 7 stringers and 5 frames. As for the reinforced panels, crack retarders made of Glare-2 2/1 0.3 were bonded to the skin under each stringer and between adjacent stringers, along the direction of stringers. An initial circumferential skin crack with a length of 25.4 mm was introduced in the middle of each panel. Fatigue crack growth tests were conducted at axial constant amplitude loads till the crack tips approached the adjacent stringers. Static tests were performed as well to determine the residual strength of the panels with two-bay skin crack. Significant retardation was found for the reinforced panels with bonded crack retarders. With the same skin stress, the average fatigue crack growth life of reinforced panels was about 2.7 times of that of baseline panels. The residual strength of reinforced panels was over 37% higher than that of baseline panels. The fatigue crack growth behavior was also predicted based on finite element model and virtual crack closure technique. The residual strength was analyzed based on modified net-section criterion. Probable reasons for certain discrepancies were discussed.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Influence of Bonded Crack Retarders on Damage Tolerance Performance of Fuselage Panel


    Beteiligte:
    Zhang, Haiying (Autor:in) / Dong, Dengke (Autor:in) / Wei, Yulong (Autor:in) / Zang, Weifeng (Autor:in) / Yan, Wenwei (Autor:in)


    Erscheinungsdatum :

    03.07.2019


    Format / Umfang :

    11 pages





    Medientyp :

    Aufsatz/Kapitel (Buch)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch






    Life Extension Techniques for Aircraft Structures - Extending Durability and Promoting Damage Tolerance through Bonded Crack Retarders

    Irving, P.E. / Zhang, X. / Doucet, J. et al. | British Library Conference Proceedings | 2011


    Bonded and prestressed fatigue crack retarders based on Fe-SMA

    Wang, Wandong / Guo, Xinlu / Zhou, Wei et al. | TIBKAT | 2024

    Freier Zugriff

    Durability and damage tolerance of bonded repairs to metallic fuselage structure

    Bakuckas, J.G. / McIver, K. / Hsu, C. | British Library Conference Proceedings | 2009