Abstract We present a meshless Crack Particles Approach (CPM) for ductile material failure. Material failure is modeled by enrichment of the meshless shape functions in the CPM where the crack is described as set of plane crack facets passing through the entire domain of influence of the meshless node. The CPM does not require any geometrical description of the crack surface. The Gurson-Tvergaard-Needleman (GTN) model is used to describe the constitutive material in the intact continuum. The onset of unstable material behavior is modeled by the loss-of-material-stability criterion. The approach is applied to two benchmark examples demonstrating the excellent accuracy of the proposed framework.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    A meshless Cracking Particles Approach for ductile fracture


    Beteiligte:
    Kumar, V. (Autor:in) / Drathi, R. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2013-12-27


    Format / Umfang :

    11 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    A meshless Cracking Particles Approach for ductile fracture

    Kumar, V. / Drathi, R. | Online Contents | 2014



    Erratum to: A meshless cracking particles approach for ductile fracture

    Kumar, V. / Drathi, R. | Springer Verlag | 2016

    Freier Zugriff

    IMECE2003-41767 Meshless Analyses of Fracture, Plasticity and Impact

    Eskandarian, A. / Chen, Y. / Oskard, M. et al. | British Library Conference Proceedings | 2003


    Fracture strength of ductile metals

    BOCKRATH, G. / GLASSCO, J. | AIAA | 1974