Abstract This paper reports results on the porosity and pore size distribution of cement paste containing varying amounts of fly ash and gypsum. The water to binder ratio was 0.5. The binder consists of cement, fly ash and gypsum. 25% of the binder was replaced with a combination of fly ash and gypsum. The fly ash ranged from 0–100%. The porosity and pore size distribution of the cement pastes at 7 days of curing are reported. Increasing the amount of gypsum does not have a noticeable effect on the pore volume, however, the pore structure becomes coarser with increasing amounts of gypsum. The results were compared with those obtained at 28 days and 365 days of curing in previous investigations.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Pore size distribution of cement pastes containing fly ash-gypsum blends cured for 7 days


    Beteiligte:
    Khatib, J. M. (Autor:in) / Mangat, P. S. (Autor:in) / Wright, L. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    25.04.2014


    Format / Umfang :

    6 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Pore size distribution of cement pastes containing fly ash-gypsum blends cured for 7 days

    Khatib, J. M. / Mangat, P. S. / Wright, L. | Online Contents | 2014


    Pore size distribution of cement mortar prepared with crushed limestone sand

    Chen, Xudong / Wu, Shengxing / Zhou, Jikai | Springer Verlag | 2015


    Pore size distribution of cement mortar prepared with crushed limestone sand

    Chen, Xudong / Wu, Shengxing / Zhou, Jikai | Online Contents | 2016


    Influence of Fly Ash on Alkalinity of Pore Solution and Microstructure Characteristics of Hardened Cement Pastes

    Yan, J.J. / Li, X. / Yang, H.Q. | British Library Conference Proceedings | 2013


    Pore size and pore size distribution on the surface of polyethersulfone hollow fiber membranes

    Tinghui Liu / Shuguang Xu / Donghua Zhang et al. | Tema Archiv | 1991