Use of graphite/resin composites in engine nacelles has been restricted because the resin is flammable. Fiberglass/polyimide and graphite/polyimide laminates were treated with various phosphorylated polymers to obtain enhanced fire-resistance and high-char-yield products after exposure to a 2000°F flame for 15 minutes. Tensile, flexural shear, and interlaminar shear strengths were determined. Polymeric phosphorylated hydrazides were found to give the best fire-resistance.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fire Resistant Composites


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    World Aviation Congress & Exposition ; 2002



    Erscheinungsdatum :

    05.11.2002




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Fire Resistant Composites

    Byrd, N. R. / Rojo, A. / Amundson, S. C. et al. | British Library Conference Proceedings | 2002


    Fire-Resistant Composites

    Kourtides, D. A. / Parker, J. A. | NTRS | 1983


    Fire-resistant wood composites

    Sawko, P. M. | NTRS | 1979


    Lightweight, Fire-Resistant Graphite Composites

    Kourtides, D. A. / Parker, J. A. / MING-TA-HSU | NTRS | 1986


    Fire resistant low density composites

    Gilwee, W. / Parker, J. / Hilado, C. | Tema Archiv | 1976