In this work the effect of resistance welding parameters in thermoplastic composite materials was evaluated in terms of the resulting microstructure and fracture mechanisms of the welded joint. Processes parameters as power density and welding time were investigated. For the microstructural characterization, samples were prepared for polarized light optical microscope observations. DCB testing was performed for the determination of the fracture energy, GI, and short beam flexure as well. The results were correlated to the microstructural characteristics of the welded region, and with the fracture surface of the tested specimens. Welded specimens were also compared to solid laminates and the particularities of each fracture mechanism were discussed.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Mode I Fracture Toughness Characterization of a Resistance Welded Carbon / PPS Laminate


    Weitere Titelangaben:

    Sae Technical Papers



    Kongress:

    SAE Brasil 2010 Congress and Exhibit ; 2010



    Erscheinungsdatum :

    2010-10-06




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Fracture Toughness of Austenitic Welded Joints

    Timofeev, B. / Sorokin, A. / Kaunas University of Technology | British Library Conference Proceedings | 2007


    Inexpensive Fracture Toughness Testing of Welded Steel

    Walters, Carey L. / Coppejans, Okko J. / Hoogeland, Martijn | Springer Verlag | 2020


    Inexpensive Fracture Toughness Testing of Welded Steel

    Walters, Carey L. / Coppejans, Okko J. / Hoogeland, Martijn | TIBKAT | 2021



    Mode I Fracture Toughness of Aligned Carbon Nanotube Epoxy Nanocomposites

    Lidston, Dale L. / Parschau, Christian / Chappelle, Christine et al. | AIAA | 2016