The aim of this paper is to study of oxidation effects in creep of the Ti-6Al-4V alloy, in different atmospheres (air, nitrogen and argon). The samples were treated during 24 hours at 600°C in different atmospheres The samples treated during 24 hours at 600°C and the oxidation behavior in each atmosphere was observed. The oxidation was more aggressive in air atmosphere, forming TiO2 film in the surface. The alloy was tested in creep at 600°C in argon, nitrogen and air atmospheres using 250 MPa. The behavior of creep curves shows that useful life is better in atmospheres not so oxidant.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The Oxidation Effect in the Titanium Alloy at High Temperature


    Weitere Titelangaben:

    Sae Technical Papers



    Kongress:

    SAE Brasil 2007 Congress and Exhibit ; 2007



    Erscheinungsdatum :

    28.11.2007




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    The Oxidation Effect in the Titanium Alloy at High Temperature

    Reis, D.A.P. / da Silva, C.R.M. / Barboza, M.J.R. et al. | British Library Conference Proceedings | 2007


    Effect of titanium on high temperature oxidation resistance of niobium based alloy

    Ning, L. / Huiren, J. | British Library Online Contents | 2010




    High temperature compression deformation behavior of TB17 titanium alloy

    ZHU Hongchang / LUO Junming / ZHU Zhishou | DOAJ | 2019

    Freier Zugriff