The General Motors L850 world engine uses an induction hardened, ductile iron, camshaft. Unlike most induction hardened camshafts that are machined first and then hardened, this camshaft is deep hardened first and then machined. Using this process, the beneficial compressive surface residual stresses are extremely high.During the development of the L850 camshaft, the casting process was optimized to produce material of sufficient quality to resist quench cracking during the hardening process and to resist mechanical cracking during the machining process. Retained austenite content, residual stress profiles, hardness, microstructure and chemical composition were all characterized and optimized.This paper reviews the material and process development for this unique automotive application.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Induction Hardened Ductile Iron Camshafts


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE 2002 World Congress & Exhibition ; 2002



    Erscheinungsdatum :

    2002-03-04




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Induction hardened ductile iron camshafts

    Druschnitz,A.P. / Thelen,S. / Intermet,US | Kraftfahrwesen | 2002


    2002-01-0918 Induction Hardened Ductile Iron Camshafts

    Druschitz, A. P. / Thelen, S. / Society of Automotive Engineers | British Library Conference Proceedings | 2002


    Cast camshafts

    Engineering Index Backfile | 1936


    Testing camshafts

    Engineering Index Backfile | 1932


    Grinding camshafts

    Engineering Index Backfile | 1930