A combination of electron microscopy and Auger depth profiling techniques was found useful in characterizing the interface zones of plated aluminum alloys. The pre-electroplating procedures examined were; zincate, Alcoa 661 Process, Alstan, and phosphoric acid anodizing. Good adhesion of electrodeposited nickel can be obtained on aluminum alloys. Failure of plated specimens in peel tests is by ductile fracture of the aluminum alloy substrate, except in the case of the anodic pretreatment where failure is principally through the oxide coating. To obtain best peel test results using the anodic pretreatment, the anodizing parameters must be tailored to the specific alloy that is to be plated.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Interfacial Features of Plated Aluminum Alloys


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Burns, R. A. (Autor:in) / Cochran, W. C. (Autor:in)

    Kongress:

    1979 Automotive Engineering Congress and Exposition ; 1979



    Erscheinungsdatum :

    1979-02-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Interfacial features of plated aluminum alloys

    Cochran,W.C. / Burns,R.A. / Alcoa Lab.,Alcoa Center,US | Kraftfahrwesen | 1979


    Plated aluminum in aircraft industry

    Yates, R.F. | Engineering Index Backfile | 1941



    Nickel Plated Electrodes for Spot Welding Aluminum

    Roest, Calvin A. / Glagola, Michael A. | SAE Technical Papers | 1976


    VEHICLE COMPONENTS HAVING DEEP MESH PLATED FEATURES

    FRAYER ROB / ANDERSON MARLON / DOROGHAZI BILL MICHAEL | Europäisches Patentamt | 2018

    Freier Zugriff